THE STRESS STATE INSTABILITY FACTOR AND ITS EFFECT ON THE GROWTH OF STRESS CORROSION CRACKING DEFECTS
DOI: 10.17804/2410-9908.2018.6.249-254 In this paper, the results of in-pipe inspection of an extended section of a gas pipeline are briefly analyzed. The comparison of the number and distribution of stress corrosion defects detected in repeated passes allows us to conclude that repair work (changing the stress state) affects the stimulation of the evolution of cracks.
Acknowledgments: This work was performed within the governmental assignment from FASO Russia on the subject of Diagnostics, No. AAAA-A18-118020690196-3 Keywords: in-pipe inspection, defects, cracks, unstable stress state, repair, distribution References: 1. Sadrtdinov R.A., Rybalko V.G., Novgorodov D.V. Peculiarities of the development of stress-corrosion cracking on a pipeline section from the results of repeated in-tube nondestructive testing. Russian Journal of Nondestructive Testing, 2012, vol. 48, iss. 7, pp. 411–417. DOI: 10.1134/S1061830912070078.
2. Radionova S.G., Zhulina S.A., Kuznetsova T.A., Pecherkin A.S., Kruchinina I.A., Grazhdankin A.I. Indicators of accidents hazard at the Russian main pipelines. Bezopasnost Truda v Promyshlennosti (Occupational Safety in Industry), 2015, no. 11, pp. 62–69. (In Russian).
3. Dolgov I.A., Gorchakov V.A., Surkov Yu.P., Rybalko V.G., Surkov A.Yu. Assessing changes in stress-corrosion damageability on the basis of repeated in-tube nondestructive testing. Russian Journal of Nondestructive Testing, 2007, vol. 43, no. 1, pp. 12–20. DOI: 10.1134/S1061830907010020.
4. Gorchakov V.A. Diagnostics of corrosion damageability in a multi-strand main gas pipeline system. Cand. Tech. Sci. Thesis, Institute of Metal Physics, Ural Branch of the Russian Academy of Sciences, Ekaterinburg, 2003. (In Russian).
5. Melekhin O.N., Gryazin V.E. Evaluation of the reliability level of the gas transmission system depending on planned volumes of capital repair of the trunk gas pipeline line part. Vesti Gazovoy Nauki, 2014, no. 1 (17), pp. 13–15. (In Russian).
Article reference
Novgorodov D. V., Rybalko V. G., Shleenkov A. S. The Stress State Instability Factor and Its Effect on the Growth of Stress Corrosion Cracking Defects // Diagnostics, Resource and Mechanics of materials and structures. -
2018. - Iss. 6. - P. 249-254. - DOI: 10.17804/2410-9908.2018.6.249-254. -
URL: http://eng.dream-journal.org/issues/2018-6/2018-6_211.html (accessed: 11/03/2024).
|